Initiated chemical vapor deposition of pH responsive poly(2-diisopropylamino)ethyl methacrylate thin films

Mustafa Karamana, Nihat Çabuka
http://dx.doi.org/10.1016/j.tsf.2012.06.083

Abstract

Poly(2-(diisopropylamino)ethyl methacrylate) (PDPAEMA) thin films were deposited on low temperature substrates by initiated chemical vapor deposition (iCVD) method using tertbutyl peroxide as an initiator. Very high deposition rates up to 38 nm/min were observed at low filament temperatures due to the use of the initiator. Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy show the formation of PDPAEMA films with high retention of tertiary amine functionality which is responsible for pH induced changes in the wetting behavior of the surfaces. As-deposited PDPAEMA thin films on flat Si surface showed a reversible switching of water contact angle values between 87° and 28°; after successive treatments of high and low pH water solutions, respectively. Conformal and non-damaging nature of iCVD allowed to functionalize fragile and rough electrospun poly(methyl methacrylate) fiber mat surfaces by PDPAEMA, which creates a surface with a switching behavior between superhydrophobic and approaching superhydrophilic with contact angle values of 155 ± 3°and 22 ± 5°, respectively.

http://www.sciencedirect.com/science/article/pii/S0040609012008140?np=y&npKey=3c3bd613bb4d5dd02f6eb6f52d7b29cb2b733070a939c4eb3813e1d20aa2fecb

 

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s